性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位 | ||
|
基本性能
|
密度
|
|
ASTM D-792
|
1200
|
kg/m3 | |
|
吸水率
|
24hr,23℃
|
ASTM D-570
|
0.15
|
% | ||
|
平衡吸水率
|
23℃,相对湿度50%
|
ASTM D-570
|
0.32
|
% | ||
|
熔体流动速率
|
|
ASTM D-1238
|
10
|
g/10min | ||
|
物理性能
|
比重
|
|
ASTM D-792
|
1.20
|
| |
|
折射率
|
|
ASTM D-542
|
1.586
|
| ||
|
模具收缩率
|
|
ASTM D-955
|
0.005-0.007
|
mm/mm | ||
|
透光率
|
|
ASTM D-1003
|
89
|
% | ||
|
雾度
|
|
ASTM D-1003
|
0.7-1.5
|
% | ||
|
机械性能
|
缺口冲击强度
|
23℃
|
ASTM D-256
|
900
|
J/m | |
|
冲击强度
|
23℃
|
ASTM D-256
|
未破裂
|
| ||
|
洛氏硬度
|
|
ASTM D-785
|
73
|
M标度 | ||
|
拉伸强度
|
屈服点
|
|
ASTM D-638
|
60
|
MPa | |
|
断裂点
|
|
ASTM D-638
|
71
|
MPa | ||
|
弯曲强度
|
|
ASTM D-790
|
96
|
MPa | ||
|
拉伸模量
|
|
ASTM D-638
|
2410
|
MPa | ||
|
弯曲模量
|
|
ASTM D-790
|
2410
|
MPa | ||
|
伸长率
|
屈服点
|
|
ASTM D-638
|
60
|
% | |
|
断裂点
|
|
ASTM D-638
|
150
|
% | ||
|
落锤冲击强度
|
23℃
|
ASTM D-3763
|
87
|
J | ||
|
电气性能
|
介电强度
|
60HZ
|
ASTM D-149
|
17
|
kv/mm | |
|
对比电弧径迹指数
|
2mm
|
IEC 112
|
250
|
v | ||
|
辉光灯丝测试
|
2mm
|
IEC 695-2-1
|
850
|
℃ | ||
|
损耗因素
|
60Hz
|
ASTM D-150
|
0.001
|
| ||
|
体积电阻率
|
23℃,干
|
ASTM D-257
|
2.0×1017
|
Ω.cm | ||
|
热性能
|
热变形温度
|
退火@0.45MPa(4 mm)
|
ASTM D-648
|
144
|
℃ | |
|
热变形温度
|
退火@1.82MPa(4 mm)
|
ASTM D-648
|
141
|
℃ | ||
|
球状压良温度
|
|
IEC 598-1
|
>125
|
℃ | ||
|
线性热收缩率
|
-40℃-82℃
|
ASTM D-696
|
68×10-6
|
mm/mm/℃ | ||
|
平均燃烧程度
|
|
ASTM D-635
|
25
|
mm | ||
|
热变形温度
|
未退火@1.82MPa(4 mm)
|
ASTM D-648
|
128
|
℃ | ||
|
维卡软化点
|
50 C/hour
|
ASTM D-1525
|
149
|
℃ | ||
|
其它性能
|
需氧系数
|
|
ASTM D-2863
|
26
|
% | |
首发：广通塑胶原料网