PC 301-10物性表
规格级别:：注塑级。
原料特性：脱模性良好，中粘度。
PC 301-10物性参数
| 性能项目
| 试验条件[状态]
| 测试方法
| 测试数据
| 数据单位 |
| 基本性能
| 平衡吸水率
| 23℃，相对湿度50%
| ASTM D-570
| 0.32
| % |
| 熔体流动速率
| 300℃/1.2kg
| ASTM D-1238
| 10
| g/10min |
| 吸水率
| 24hr,23℃
| ASTM D-570
| 0.15
| % |
| 物理性能
| 阻燃等级
| 1.6mm
| UL 94
| HB
| |
| 透光率
|
| ASTM D-1003
| 89
| % |
| 折射率
|
| ASTM D-542
| 1.586
| |
| 模具收缩率
|
| ASTM D-955
| 0.005-0.007
| in/in |
| 阻燃等级
| 3.2mm
| UL 94
| HB
| |
| 比重
|
| ASTM D-792
| 1200
| kg/m3 |
| 雾度
|
| ASTM D-1003
| 0.7-1.5
| % |
| 机械性能
| 拉伸模量
|
| ASTM D-638
| 2410
| MPa |
| 落锤冲击强度
| 总能量@23℃
| ASTM D-3763
| 87
| J |
| 冲击强度
| 23℃
| ASTM D-256
| 未破裂
| |
| 弯曲强度
|
| ASTM D-790
| 96
| MPa |
| 拉伸强度
| 屈服点
| 50mm/min
| ASTM D-638
| 60
| MPa |
| 断裂点
| -
| ASTM D-638
| 71
| MPa |
| 洛氏硬度
|
| ASTM D-785
| 118
| R标度 |
| 洛氏硬度
|
| ASTM D-785
| 73
| M标度 |
| 缺口冲击强度
| 23℃
| ASTM D-256
| 900
| j/m |
| 伸长率
| 屈服点
|
| ASTM D-638
| 6
| % |
| 断裂点
|
| ASTM D-638
| 150
| % |
| 弯曲模量
|
| ASTM D-790
| 2410
| MPa |
| 电气性能
| 介电强度
| 60Hz
| ASTM D-149
| 17
| V/mil |
| 辉光灯丝测试
| 2mm，5s
| IEC 695-2-1
| 850
| ℃ |
| 体积电阻
| 23℃，干
| ASTM D-257
| 2.0×1017
| Ω.cm |
| 损耗因素
| 60Hz
| ASTM D-150
| 0.001
| |
| 球状压痕温度
|
| IEC 598-1
| >125
| ℃ |
| 对比电弧径迹指数
| 2mm
| IEC 112
| 250
| V |
| 热性能
| 热变形温度
| 未退火@1.82MPa
| ASTM D-648
| 128
| ℃ |
| 热变形温度
| 退火@1.82MPa
| ASTM D-648
| 141
| ℃ |
| 平均燃烧系数
|
| ASTM D-635
| 25
| mm |
| 维卡软化点
| 50℃/小时，50n重
| ASTM D-1525
| 149
| ℃ |
| 线性热收缩率
| -40℃～82℃
| ASTM D-696
| 68×10-6
| mm/mm/℃ |
| 热变形温度
| 退火@0.45MPa
| ASTM D-648
| 144
| ℃ |
| 其它性能
| 需氧系数
|
| ASTM D-2863
| 26
| % |