TPEE 4556物性表
规格级别：注塑级
| 性能项目
| 试验条件[状态]
| 测试方法
| 测试数据
| 数据单位 |
| 基本性能
| 24小时吸水率
|
| ASTM D-570
| 0.6
| % |
| 物理性能
| 泰伯磨耗量
| CS-17轮
| ASTM D-1044
| 3
| mg/1000rev |
| 比重
|
| ASTM D-792
| 1.14
| |
| 泰伯磨耗量
| H 18轮
| ASTM D-1044
| 72
| mg/1000rev |
| 熔体流动速率
|
| ASTM D-1238
| 8.5
| g/10min |
| 机械性能
| 初耐撕裂性能
|
| ASTM D-1004
| 116
| kn/m |
| 拉伸力
| 5%伸长
|
| ASTM D-638
| 4.1
| Mpa |
| 10%伸长
|
| ASTM D-638
| 5.7
| Mpa |
| 埃佐冲击强度
| 23℃
| ASTM D-256
| 不破裂
| J/m |
| 断裂伸长
|
| ASTM D-638
| 600
| % |
| 揉曲模量
| 23℃
| ASTM D-790
| 94
| Mpa |
| 断裂拉伸力
|
| ASTM D-638
| 31
| Mpa |
| 硬度计硬度
|
| ASTM D-2240
| 45
| |
| 热性能
| 熔点
|
| ASTM D-3418
| 193
| ℃ |
| 维卡软化点
|
| ASTM D-1525
| 158
| ℃ |
| 热畸变温度
| @0.18Mpa
| ASTM D-648
| 43
| ℃ |
| 热畸变温度
| @0.5Mpa
| ASTM D-648
| 60
| ℃ |
| 其它性能
| 耐揉曲切口增长性能
|
| ASTM D-1052
| >1×106
| |