TPEE 555HS物性表
规格级别：热稳定级。
| 性能项目
| 试验条件[状态]
| 测试方法
| 测试数据
| 数据单位 |
| 基本性能
| 24小时吸水率
|
| ASTM D-570
| 0.7
| % |
| 物理性能
| 泰伯磨耗量
| CS-17轮
| ASTM D-1044
| -
| mg/1000rev |
| 热畸变温度
| @0.5Mpa
| ASTM D-648
| 90
| ℃ |
| 熔体流动速率
|
| ASTM D-1238
| 8.5
| g/10min |
| 泰伯磨耗量
| H 18轮
| ASTM D-1044
| 112
| mg/1000rev |
| 比重
|
| ASTM D-792
| 1.20
| |
| 机械性能
| 揉曲模量
| 23℃
| ASTM D-790
| 207
| Mpa |
| 拉伸力
| 5%伸长
|
| ASTM D-638
| 6.9
| Mpa |
| 10%伸长
|
| ASTM D-638
| 10.3
| Mpa |
| 埃佐冲击强度
| 23℃
| ASTM D-256
| 不破裂
| J/m |
| 硬度计硬度
|
| ASTM D-2240
| 55
| |
| 初耐撕裂性能
|
| ASTM D-1004
| 158
| kn/m |
| 断裂拉伸力
|
| ASTM D-638
| 40
| Mpa |
| 断裂伸长
|
| ASTM D-638
| 500
| % |
| 热性能
| 维卡软化点
|
| ASTM D-1525
| 180
| ℃ |
| 热畸变温度
| @0.18Mpa
| ASTM D-648
| 49
| ℃ |
| 熔点
|
| ASTM D-3418
| 203
| ℃ |
| 其它性能
| 耐揉曲切口增长性能
|
| ASTM D-1052
| >1×105
| |