性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位 | |
|
基本性能
|
熔体流动速率
|
|
|
9
|
g/10min |
|
吸湿率
|
|
ASTM D-570
|
0.2
|
% | |
|
物理性能
|
成型收缩率
|
|
旭化成方法
|
1.6-2.0
|
% |
|
比重
|
|
ASTM D-792
|
1.41
|
| |
|
磨耗率
|
|
ASTM D-1044
|
14
|
mg/1000cycles | |
|
机械性能
|
缺口冲击强度
|
|
ASTM D-256
|
7
|
J/m |
|
抗挠强度
|
|
ASTM D-790
|
88
|
MPa | |
|
洛氏硬度
|
|
ASTM D-785
|
115
|
R Scale | |
|
拉伸模量
|
|
ASTM D-790
|
2800
|
MPa | |
|
断裂拉伸强度
|
|
ASTM D-638
|
66
|
MPa | |
|
洛氏硬度
|
|
ASTM D-785
|
80
|
M-Scale | |
|
断裂伸长率
|
|
|
55
|
% | |
|
热性能
|
热变形温度
|
1.8MPa
|
ASTM D-648
|
100
|
℃ |
|
阻燃性
|
|
UL 94
|
HB
|
| |
|
热变形温度
|
0.45MPa
|
ASTM D-648
|
156
|
℃ | |